Lotherme-210r Carbon And Low Alloy Steels Welding Rod

Name: Lotherme-210r Carbon And Low Alloy Steels Welding Rod
Brand: D & H SECHERON ELECTRODES PRIVATE LIMITED
Price: 525.00 INR
Availability: InStock

Price 525.00 INR/ Kilograms

Get a Price/Quote

MOQ : 10 Kilograms, ,

Lotherme-210r Carbon And Low Alloy Steels Welding Rod Specification

Composition
Optimized carbon, manganese, and silicon for weld ductility

Operating Voltage
Open Circuit Voltage (OCV) 50 V min

Application
General fabrication, maintenance welding, piping, pressure vessels, tanks

Operating Temperature
Room temperature to 350C (preheat as recommended)

Material
Carbon and Low Alloy Steels

Diameter
2.5 mm, 3.15 mm, 4.0 mm, 5.0 mm

Flux Content
High rutile type flux coating

Melting Point
Approximately 1500C

Coating
Medium heavy, rutile type

Elongation
Up to 27%

Current Type
AC / DC (+)

Tensile Strength
Up to 540 MPa

Packing
Standard 5 kg and 15 kg boxes

Welding Position
Flat, horizontal, vertical up & overhead

Storage
Store in dry condition; re-dry electrodes if moisture pickup is suspected

Recommended Polarity
Direct Current Electrode Positive (DCEP) or Alternating Current (AC)

About Lotherme-210r Carbon And Low Alloy Steels Welding Rod

We are one of the leading manufacturers of Lotherme-210r Carbon And Low Alloy Steels Welding Rod in the market. It has been designed for welding sheet metal in low heat input technique. Lotherme-210r Carbon And Low Alloy Steels Welding Rod can also be used for welding mild steel of higher thicknesses depending on the applications.

Versatile Welding Solution

Lotherme-210r rods can be used for various applications including general fabrication, maintenance, piping, and vessel welding. The product's compatibility with AC and DC (+) currents, multiple diameters, and rutile flux coating ensures adaptability to diverse fabrication and repair projects.

Optimal Strength and Ductility

Engineered with carbon, manganese, and silicon, Lotherme-210r delivers tensile strength up to 540 MPa and elongation up to 27%. Its unique flux composition assures durable and ductile welds, suitable for components exposed to dynamic loading and pressure.

Reliability and Storage

To maintain the electrode's high performance, it should be stored in dry conditions. If moisture is suspected, re-drying is recommended. Conveniently packed in 5 kg and 15 kg boxes, these rods are ready for use, minimizing downtime and ensuring consistent weld quality.

FAQ's of Lotherme-210r Carbon And Low Alloy Steels Welding Rod:

Q: How should Lotherme-210r welding rods be stored to maintain optimal performance?

A: Lotherme-210r electrodes should be stored in a dry environment to prevent moisture absorption. If there is any suspicion that the rods have absorbed moisture, it is advisable to re-dry them before use to maintain weld integrity and avoid defects.

Q: What types of welding positions are suitable when using Lotherme-210r rods?

A: Lotherme-210r rods are designed for flexible usage and can be employed in flat, horizontal, vertical up, and overhead welding positions, making them versatile for a variety of fabrication and maintenance tasks.

Q: When is preheating recommended before welding with Lotherme-210r?

A: Preheating is recommended for thicker sections or materials sensitive to cracking, particularly those operating at or below room temperature up to 350C. This practice helps optimize weld quality and reduce the risk of thermal stress.

Q: Where can Lotherme-210r welding rods be used effectively?

A: Lotherme-210r is suitable for general fabrication, maintenance welding, piping, pressure vessel production, and tank construction in industrial environments requiring reliable welds on carbon and low alloy steels.

Q: What current type and polarity should be used for Lotherme-210r?

A: The recommended current types are Alternating Current (AC) or Direct Current Electrode Positive (DCEP). Ensure that the welding machine provides a minimum open-circuit voltage of 50 V for optimal performance.

Q: How does the high rutile flux coating benefit the welding process?

A: The medium-heavy, high rutile flux coating provides excellent arc stability, smooth slag removal, and helps in producing clean, ductile welds with minimal spatter, contributing to efficient and high-quality welding operations.

Q: What diameters are Lotherme-210r rods available in and how do you select the appropriate size?

A: Lotherme-210r rods are available in 2.5 mm, 3.15 mm, 4.0 mm, and 5.0 mm diameters. The selection depends on the thickness of the workpiece and the requirements of the welding application, with larger diameters suited for thicker materials.