D And H Monel Cast Iron Electrodes

Name: D And H Monel Cast Iron Electrodes
Brand: D & H SECHERON ELECTRODES PRIVATE LIMITED
Price: 4875.00 INR
Availability: InStock

Price 4875.00 INR/ Kilograms

Get a Price/Quote

MOQ : 10 Kilograms

D And H Monel Cast Iron Electrodes Specification

Operating Temperature
Ambient to 350C

Application
Joining and repairing Monel to cast iron, cast iron to steel, and broken, cracked or worn-out machine parts

Composition
Nickel (Ni) 65-70%, Copper (Cu) 30-35%, Iron (Fe) <3%

Operating Voltage
70V 90V (AC/DC)

Material
Monel Cast Iron

Diameter
3.15 mm, 4.00 mm, 5.00 mm

Flux Content
Specially formulated flux suitable for Monel and cast iron applications

Melting Point
1300C - 1450C

Coating
Heavy-duty rutile base coating

Penetration
Moderate to Deep

Storage Instructions
Store in a dry place below 30C

Density
Approx. 8.8 g/cm3

Welding Position
All positions (Flat, Horizontal, Vertical, Overhead)

Packaging
1 kg, 2.5 kg, 5 kg boxes

Current Range
90A - 180A

Arc Stability
Excellent arc stability and low spatter

Color of Deposit
Silver Grey

Shelf Life
12 months from date of manufacturing

Tensile Strength
Up to 550 MPa

D And H Monel Cast Iron Electrodes Trade Information

Minimum Order Quantity
10 Kilograms

Supply Ability
1000 Kilograms Per Day

Delivery Time
1 Week

About D And H Monel Cast Iron Electrodes

We are a trustworthy manufacturer of D And H Monel Cast Iron Electrodes in the market. These are suitable to weld carbon steel to cast iron, broken casting repairs, machining defect rectification, filling up castings and also rebuilding worn out surfaces. D And H Monel Cast Iron Electrodes are machine bases, engine blocks, pumps, gears etc.

Superb Arc Stability and Low Spatter

D And H Monel Cast Iron Electrodes are engineered to deliver stable arcs with minimal spatter, giving welders greater control over the welding process. This feature not only enhances weld quality but also reduces clean-up time, making the electrodes suitable for both professional and industrial applications.

Versatility Across Welding Positions

With support for all standard welding positionsflat, horizontal, vertical, and overheadthese electrodes offer flexibility for a wide variety of tasks. Whether repairing worn machinery or joining dissimilar metals, they provide the adaptability required in fabrication and maintenance shops.

FAQs of D And H Monel Cast Iron Electrodes:

Q: How should D And H Monel Cast Iron Electrodes be stored for optimal shelf life?

A: To ensure maximum shelf life and performance, store the electrodes in a dry environment at temperatures below 30C. This helps prevent moisture absorption and maintains the integrity of the flux coating for up to 12 months from the manufacturing date.

Q: What are the recommended welding positions and current range for using these electrodes?

A: These electrodes are suitable for all welding positions, including flat, horizontal, vertical, and overhead. The recommended current range is 90A to 180A, with an operating voltage of 70V 90V on either AC or DC power sources.

Q: When is it appropriate to use D And H Monel Cast Iron Electrodes?

A: These electrodes are ideal for joining or repairing Monel to cast iron, cast iron to steel, and for fixing broken, cracked, or worn machine parts. Their specially formulated flux ensures compatibility across these challenging applications.

Q: Where are D And H Monel Cast Iron Electrodes most commonly used?

A: They are widely used in industrial repair shops, manufacturing units, and maintenance sectors throughout India where robust and reliable welds for cast iron and Monel are required.

Q: What is the benefit of the heavy-duty rutile base coating and specially formulated flux in these electrodes?

A: The heavy rutile base coating and unique flux formulation enhance arc stability, reduce spatter, and allow moderate to deep penetration, resulting in strong, high-quality weld beads suitable for critical repairs and fabrications.

Q: How does the electrodes material composition enhance its welding performance?

A: With a composition of 65-70% Nickel, 30-35% Copper, and less than 3% Iron, the electrodes provide excellent corrosion resistance and strength, making them ideal for demanding fabrication and repair tasks.